Glass Fiber Reinforced Polyvinyl Chloride Sheet

Glass Fiber Reinforced Polyvinyl Chloride Sheet

1.Product overview The PVC membrane is made by using polyvinyl chloride resin as main material, blended in defoamer, aging resisting agent and ultraviolet light absorber.While Adding fiberglass mesh, fiberglass non-woven fabrics as inner reinforcement, the product has been greatly enhanced in...

Product Details

Glass Fiber Reinforced Polyvinyl Chloride Sheet

1.Product overview
 The PVC membrane is made by using polyvinyl  chloride resin as main material, blended in defoamer, aging resisting agent and  ultraviolet light absorber.While Adding fiberglass mesh, fiberglass non-woven  fabrics as inner reinforcement, the product has been greatly enhanced in its  tensile strength and durability,which makes it applicable for high-requirement  and complicated waterproofing engineering.

QQ图片20170918113637_副本.jpg   

 
















2.Application  scope
 1)Tunnels  waterproofing of subway, road or rail way, bridges, civil air defense  engineering, etc.
 2)Industrial/  civil building basement and roof waterproofing, roofing engineering includes  plant roof, flat roof, sloping roof, concrete roof, light steel structure roof  as well as the interior & exterior roof.
 3)Large  grain depot, beam field, landfill, artificial lake, pipe trenches &  municipal engineering of waterproof, etc.


image008.jpgimage010.jpgimage012.jpg

       

3.Product Features
 1)After added with fiber glass,the product  has longer service life, high tensile strength & elongation, It can  effectively resist the destruction of the waterproof layer due to structure  deformation.
 2)Superior aging-resistance,low deformation  rate to heat,good resistance to wind-uplift, specially applicable for exposed  roof system.
 3)Good resistance to perforation and  mechanical damage.
 4)Resistance to chemical corrosion &  mildew, especially applicable to tunnel waterproofing and planting roof  waterproof engineering.
 5)Good low temperature flexibility, flame  retardant, self-extinguishing once deviated from fire,  
 high construction safety and reliability.

  1. Bond well with substrate after hot gas welding, reliable seam  welding, Eco-friendly.

 

4.Executive standard & Performance index

Executive    standard: GB12952-2011  PVC Waterproof Membrane

Item

Index

H

L

P

G

Top side resin thickness/mm     ≥

-

0.40

Tensile property

Maximum Tension/(N/cm) ≥

-

120

250

-

Tensile Strength/Mpa  ≥

10.0

-

-

10.0

Max Elongation Rate/%  ≥

-

-

15

-

Elongation at Break/%  ≥

200

150

-

200

Heat-treatment size change rate/%  ≤

2.0

1.0

0.5

0.1

 Cold Bending

-25℃,no crack

Water Tightness

0.3Mpa,2h, no leakage

 Impact-resistance

0.5kg·m,no leakage

Joint Peel Strength/(N/mm)     ≥

4.0 or material damage

3.0

Right Angle Peel Strength/(N/mm)     ≥

50

-

-

50

Trapezoidal Tear Strength/N     ≥

-

150

250

-

Water absorption(70℃,168h)/%

After immersion  ≤

4.0

After open time  ≤

-0.40


5.Product Specification

Thickness/mm

1.2

1.5

1.8

2.0

Width/mm

1000/2000

1000/2000

1000/2000

1000/2000

Length/m

20/25

20/25

20

15


6.Storage
 1)Different types  and specifications of the products should be stacked respectively. Pay  attention to ventilation. Storage temperature should not be higher than 45℃, flat storage stack  height no more than five layer, put single pile vertical, keep product away  from acid, alkali, oil, organic solvent, etc.
 2)Transportation  to prevent tilt or lateral pressure, cover with cloth if necessary.
 3)Under  the condition of normal storage & transportation, storage period is one  year.