Crystalline Concrete Building Waterproofing

Crystalline Concrete Building Waterproofing

Crystalline concrete waterproofing coats Introduction of Crystalline concrete waterproofing coats Cementitious Capillary Crystalline Waterproofing Coating is a rigid waterproofing material made using high-grade cement and fine quartz sand as main materials, adding in many imported reactive...

Product Details

Crystalline Concrete Building Waterproofing

 Crystalline concrete waterproofing coats 


image004.jpg


  • Introduction  of Crystalline concrete waterproofing coats

Cementitious Capillary Crystalline  Waterproofing Coating is a rigid waterproofing material made using high-grade  cement and fine quartz sand as main materials, adding in many imported reactive  chemicals as penetration masterbatch. It is a powder looking material and shall  be mixed with water just prior to application.


  • What  about the product

  • Anti-penetration of the product is great; performance on both sides  of structure is excellent.

  • The product is ageing resistant, acid resistant and alkali  resistant.

  • The product can be used on moisture/damp surface.

  • Ability to fill tiny cracks in concrete, permanent activity.

  • This product is suitable for tiles.

 

  • Where  to use

  • Civil and industrial building waterproofing

  • Transportation system waterproofing

  • Various water pools, ponds.

  • Different municipal engineering.

  • How  to use

  • Application substrate need to be hard surface and clean, and the  ambient temperature is between 5℃ to 35℃.

  • Wet out the substrate before product application, but do not leave  any water ponding on the surface.

  • This product need to mix with water before application, mixing ratio  is 2.4~3:1(powder: water).

  • It is recommended to carry out this coating process in 2 to 3  separate passes. Only do the next pass when the previous pass is slightly  cured, usually an interval of 3 to 4 hours is needed. If an excessive interval  is inevitable, the previous pass needs to be wet out before doing the next  pass.

  • After the construction is finished, keep the waterproof layer wet  for no less than 3 days as a maintenance.

 

  • Executive  standard

Executive standard:GB18445-2012 Cementitious    Capillary Crystalline Waterproofing Coating

Item

Index

Appearance feature

Uniform powder, no caking

Water content  ≤

1.5%

Finess, 0.63mm residue on sieve  ≤

5%

Chlorine ion content  ≤

0.10%

Operability

Mixed with water

knife coating barrier-free

After 20min

knife coating barrier-free

Breaking strength in 28d  ≥

2.8Mpa

Compressive strength in 28d  ≥

15.0Mpa

Bonding strength at damp surface in 28d  ≥

1.0Mpa

 

6. Cautions

  • The construction of the product requires ambient temperature to be  higher than 5℃.

  • Once the package is open, use up the product as soon as possible. Do  not leave any left product unsealed.

  • The waterproof layer shall be well protected before it is full  cured.


7. Storage

  • Keep the product in a shady place, with temperature between 10℃ to 45℃.

  • Storage life of the product is one year. But the product still be  usable if in good condition even if after storage life.

  • This is an odorless, non-flammable and non-toxic product. It must be  place upright either in transportation or storage.